Pre Shaded Multilayer Zirconia Block 750MPa Bending Strength Ultra Translucent Zirconia

Basic Information
Place of Origin: China
Brand Name: XTCERA
Certification: FDA,CE,SFDA,ISO 19485
Minimum Order Quantity: 50 PCS
Price: Negotiable
Packaging Details: box
Delivery Time: 5-8 working days
Payment Terms: T/T, Western Union, MoneyGram
Supply Ability: 3000pc/week
Detail Information
Sintering Density: ≥6.0g/cm³ Bending Strength: ≥750MPa
Transmittance: 55% Vickers Hardness: 1250HV
Size: Customer Size Usage: PROFESSIONAL DENTAL
High Light:

ultra translucent zirconia

,

cerec zirconia blocks


Product Description

Multilayer TT Zirconia Blanks
 
Advantage of zirconia dental:
1. High aesthetic effect, good transparency, natural tooth color.
2. High strength, hardness and durable, do not need the support of metal.
3. Excellent biological compatibility, no metal odor, no black color and no corrosion, anti allergy, protect the gums and avoid bleeding.

 

 

The zirconia disk and blocks are the finest and most pure zirconia materials , most of zirconia powder are from Japan and well compatible with all open cad cam milling machine,like Origin milling machine,Shera Milling machine.VHF milling machine.

1.All of zirconia disks with super high translucence (light transmittance 40%) are for full contour.
2.All of zirconia block with High translucence (light translucence 30%) are for dental coping and bridge.

 

 

Perfect Your Smile!
 

Layer Proportion

Vickers
Hardness(HV)

Strength(MPa) Color Translucency
Layer 1 30% ≥1250 ≥750

Shallow
 

 
Deep

55%
Layer 2 15%
Layer 3 15%
Layer 4 20%
Layer 5 20%

 
Characteristics:
Top High Transmittance
Natural Color Transition, Pre-colored.
Simple and Less Process of Production
 
Available in all classic VITA 16 shades (A1 to D4)
Indications
XTCERA TT Multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, inlays and onlays restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.

 
 
Chemical Composition
 

Component Content
ZrO2+HfO2 >90.5wt%
Y2O3 9.28wt%
AL2O3 <0.5wt%
Other Oxides <0.5wt%

 
Properties
 

Projects Detection result
Sintering Density ≥6.0g/cm³
Bending Strength ≥750MPa
Transmittance 55%
Vickers Hardness 1250HV

 
 
 

Sintering step Temperature range (℃) Time(h)
paragraph 1 20-900 1.5
paragraph 2 900-900 0.5
paragraph 3 900-1450 3.0
paragraph 4 1450-1450 2.0
paragraph 5 1450-800 1.0
paragraph 6 800-Natural cooling 100 Finished